13549213581肖生

 

FDA食品接触,抗氧化性, 良好的撕裂强度, 高密度, 抗穿孔性, 光学性能, 拉伸缠绕, 流延薄膜

 

SABIC® LLDPE 6318BE

线性低密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

Technical Data

 

产品说明

SABIC® LLDPE 6318BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Films produced from this grade exhibit excellent optical properties, toughness, puncture resistance and tear strength. The suffix E denotes European origin.

 

SABIC® LLDPE 6318BE resin is recommended for pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required. The grade is also suggested for blending with ethylene/butene copolymer LLDPE and LDPE for improving strength.

 

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing - Cast Film (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Saudi Basic Industries Corporation (SABIC)

供货地区 • 欧洲

添加剂 • 抗氧化性

• 高强度 • 抗穿孔性 • 热稳定性，良好

特性 • 光学性能 • 抗氧化性 • 韧性良好

• 己烯共聚单体 • 良好的撕裂强度 • 食品接触的合规性

用途 • 混合 • 拉伸缠绕 • 流延薄膜

形式 • 粒子

加工方法 • 流延薄膜

 

物理性能 额定值单位制 测试方法

密度 0.920g/cm³ ISO 1183/A

熔流率（熔体流动速率） (190°C/2.16 kg) 3.2g/10 min ISO 1133

薄膜 额定值单位制 测试方法

薄膜厚度 - 经测试 20µm

Elastic Recovery 3 (20.0 µm) 56% ASTM D5459

Protrusion Puncture Resistance 3 (20.0 µm) 2.70J ASTM D5748

Retention Force - 60 sec 3 (20.0 µm) 950g

Stress Retention 3 (20.0 µm) 78% ASTM D5459

Ultimate Pre-stretch Level 3 (20.0 µm) 290%

热性能 额定值单位制 测试方法

维卡软化温度 105°C ISO 306/A

溶融温度（DSC） 125°C 内部方法

光学性能 额定值单位制 测试方法

光泽度 (45°, 20.0 µm, 铸造薄膜) 90 ASTM D2457

雾度 (30.0 µm, 铸造薄膜) 1.8% ASTM D1003A

补充信息 额定值单位制 测试方法

Dart Impact 3 (20.0 µm) 18.0J/cm ISO 7765-2

Peel Cling 3 ASTM D5458

0% pre-stretch : 20.0 µm 229.4g/2.5 cm

200% pre-stretch : 20.0 µm 102.0g/2.5 cm

Tear Strength - TD 3 (20.0 µm) 246.0kN/m ISO 6383-2

Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch line: melt temperature 270 °C, chill roll

temperature 20 °C and line speed 450 m/min.

挤出 额定值单位制

熔体温度 285 到 310°C

 

 

 

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料线性低密度聚乙烯  SABIC 基础创新塑料(美国) SABIC® LLDPE 6318BE因为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。